Incoloy 925 flange,ASTM B564 Incoloy 925 Flanges,N09925 Weld neck Flange,Slip on Flange,Blind flange
ASTM B564 UNS N09925, also known as Incoloy 925, an age- hardenable nickel-iron-chromium alloy with additions of molybdenum, copper, titanium and aluminum.
INCOLOY alloy 925 (UNS N09925) with the additions of molybdenum, copper, titanium and aluminium is an age hardenable nickel-iron-chromium alloy, providing a combination of high strength and excellent corrosion resistance. Sufficient nickel content provides protection against chloride-ion stress-corrosion cracking whilst in conjuncton with the added molybdenum and copper resistance to reducing chemicals is enjoyed. Molybdenum additionally aids resistance to pitting and crevice corrosion whilst Chromium offers resistance to oxidizing enviroments
| Incoloy 925 Slip On Flanges | Incoloy 925 Weld Neck Flanges |
| Incoloy 925 weld neck rtj Flanges | Incoloy 925 blind flange |
| Alloy 925 BLRF Flanges | Incoloy 925 orifice flange |
ASTM B564 UNS N09925 Chemical composition:
Chemical Composition,%
| C | P | S | Mn | Si | Cr | Ni | Mo | Al | Ti | Cu | Fe |
|---|---|---|---|---|---|---|---|---|---|---|---|
| ≤0.03 | ≤0.03 | ≤0.03 | ≤1.00 | ≤0.50 | 19.50~22.50 | 42.00~46.00 | 2.50~3.50 | 0.10~0.50 | 1.90~2.40 | 1.50~3.00 | Bal |
Typical Physical & Mechanical Properties
| Density, g/cm3 | Melting Point, ℃ | Tensile Strength, MPa | Yield Strength, MPa | Elongation,% |
|---|---|---|---|---|
| 8.08 | 1311-1366 | 1210 | 810 | 24 |
Please drop inquiry to bill@cnpipefitting.com
Production range |
|||||
ASME B16.5 ASTM B 564UNS N09925 FlangeINCOLOY 925 Flange |
Size:1/2″-24″ Wall thickness:SCH5S-SCHXXS Class:150-1500# | ||||
| ASME B16.47 ASTM B 564 UNS N09925 Flange
INCOLOY 925 Flange |
Size:26″-48″ Wall thickness:SCH5S-SCHXXS Class:150-1500# | ||||
| ASME B16.48 ASTM B 564 UNS N09925 Flange
INCOLOY 925 Flange |
Size:1/2″-24″ Wall thickness:SCH5S-SCHXXS Class:150-1500# | ||||
MSS SP-44
ASTM B 564 UNS N09925 FlangeINCOLOY 925 Flange |
Size:12″-60″ Wall thickness:SCH5S-SCHXXS Class:150-1500# | ||||