We provide  good quality Incoloy A-286 stud bolts, Incoloy A-286 threaded rod, Incoloy A-286 threaded bar, Incoloy A-286 double ends stud bolts… in full thread or half thread. Our standards/specifications covers ASTM, ASME, DIN, ISO. Such as DIN975, DIN976, DIN938,  DIN939, ASME/AISI 18.2.1 etc

Incoloy A-286 stud bolt is a Fe-25Ni-15Cr based superalloy with comprehensive strengthening of molybdenum, titanium, aluminum, vanadium and trace boron. It has high yield strength and long-lasting, creep strength below 650 ° C, and has good processing plasticity and satisfactory welding performance. Suitable for the manufacture of high-temperature bearing components for aerospace engines operating at temperatures below 650 °C, such as turbine disks, compressor disks, rotor blades and fasteners.

Alloy A286 is a precipitation hardening that combines high strength and good corrosion resistance, austenitic stainless steel designed for use at temperatures up to 1300°F (704°C) , where high tensile strength, excellent creep strength and good corrosion resistance are required. LSS™ A286 is available in a wide range of ingot, billet, bar, and coil rod sizes. Bar is available as either rounds or flats.

A286 alloy provides high strength up to a temperature of 1300° F and corrosion resistance up to a constant temperature of 1500° F or an intermittent temperature of 1800° F. A286, which is a ductile, non-magnetic, iron-based alloy, can reach its highest strength level through solution heat treating and age hardening. Because it is a higher strength metal, greater pressureis required when forming. It is best to weld and form A286 in the solution treated condition. Before machining A286, it is best to solution treat and cold working the material first.

A286 alloy is a heat and corrosion resistant austenitic ironbase material which can be age hardened to a high strength level. The alloy is also used for low temperature applications requiring a ductile, non-magnetic high strength material at temperatures ranging from above room temperature down to at least -320°F (-196°C). The alloy may be used for moderate corrosion applications in aqueous solutions. Type A286 alloy can be produced by AOD refining or vacuum induction melting. Vacuum arc or electroslag remelting procedures may be used to further refine the material. Type A286 alloy is available in plate, sheet and strip.

A286 is an iron-nickel-chromium alloy with additions of molybdenum and titanium. A 286 is one of the most popular high temperature alloys. As one of the austenitic alloys it maintains good strength and oxidation resistance at temperatures up to 1300ºF. Due to it’s high strength and excellent fabrication characteristics A286 is used in various components of aircraft and industrial gas turbines. A286 is also widely used in the offshore oil and gas industry where the components are subject to high levels of heat and stress.

Alloy A286 Chemical Composition