Aluminum 6061-T6 Angle bar,Aluminium Alloy Sngle Bar 6061 T6
Angle aluminum or Aluminum ange bar is also a general aluminum profile, which is widely used in many fields, such as architecture, decoration, industry, usually used instead of Angle iron. Angle aluminum is not necessarily of equal length on both sides, and also see angular aluminum with rounded corners, they have their own special use.
6061 T6 angle bar aluminum is light-weight, soft and corrosion resistant. It is a great conductor of both heat and electricity. Aluminum 6061 T6 angle bar is also easy to weld, cut and machine, which makes it great for a bevy of applications.
6061-T6 Angle bar
is an extruded aluminum product that is very versatile and has a wide range of applications. 6061 Aluminum angle is made from one of the most widely used heat treatable aluminum alloys. It has excellent corrosion resistance, good workability and good machinability. 6061 aluminum structural angle applications include a wide variety of products from medical assemblies, aircraft construction to structural components. 6061 t6 aluminum angle has a high strength to weight ratio making it ideal for any application where parts need to be light.
6061 T6 Chemical Composition
| % | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Al |
| Min | 0.40 | 0.15 | 0.80 | 0.04 | |||||
| Max | 0.80 | 0.70 | 0.40 | 0.15 | 1.20 | 0.35 | 0.25 | 0.15 | Remainder |
Standard Specification: GB/T 6892, ASTM B221, EN754, EN 755
| Alloy | Temper |
| 5xxx: 5083 | O, H112 |
| 6xxx: 6005, 6060, 6061, 6063, 6082,6463 | T5, T6, T66 |
Alloy Designation (For Reference)
Comparison of Alloy Designations for Aluminum Products
| Alloy Series | Chinese Standard | American Standard | European Standard |
| 5xxx Series | 5083 | 5083 | EN AW-5083 |
| 6xxx Series | 6005 | 6005 | |
| 6060 | 6060 | EN AW-6060 | |
| 6061 | 6061 | EN AW-6061 | |
| 6063 | 6063 | EN AW-6063 | |
| 6082 | 6082 | EN AW-6082 | |
| 6463 | 6463 | EN AW-6463 |
Temper Designation (For Reference)
| Temper | Definition |
| O | Annealed |
| H112 | Slightly strain harden from working at an elevated temperature or from limited amount of cold work |
| T5 | Cooled from an elevated temperature shaping process and then artificially aged |
| T6 | Solution heat-treated and then artificially aged |
| T66 | Solution heat-treated and then artificially aged – mechanical property level higher than T6 achieved through special control of the process (6000 series alloys) |
Available Size Range
| Dimension | Range |
| A | 10mm~200mm |
| B | 10mm~200mm |
| T | 2mm~15mm |
| Length | 1,000~6,000mm |